Solvent Based Acrylic Floor Coatings Resin
SE6773 is a two-component hydroxyl acrylic resin, by combining with
isocyanate curing agent, the coating produced has high gloss, high
fullness, good adhesion with the substrate, has strong
anti-ultraviolet function, it won’t chalking and yellowing, its
film properties and outdoor resistance to the sun is also very
prominent, it belongs to a seamless self-levelling coating system.
Recommended for:
- Floor coating on concrete surfaces
- Industrial floor and warehouse floor
- The pavement etc.
- Badminton court, tennis court
1. Features
High gloss, high fullness, good levelling property, excellent
weather resistance, excellent chemical resistance, ABS one-time
spraying
2. Applications
PU varnish, aluminium powder paint, automobile refinishing paint
3. Properties
| Component | Appearance | Fe-Co
Color | Viscosity
Pa.s/25℃ | Non-volatile
% | Acid value
mgKOH/g | Solvent | Hydroxyl value |
| Acrylic copolymer | Clear and
transparent | ≤1 | 3-7 | 65±2 | 4-10 | XYL/BAC | 100 |
4. Compatibility and solubility
| SE6631 | + | SE6771 | + | XYL | + | BCS | + |
| SE6672 | + | SE6530 | + | TYL | + | CAC | + |
| SE6570 | + | SE6650 | + | BAC | + | CYC | + |
| | | | PMA | + | NBA | + |
Remark:+ show soluble in/compatible in
5. Reference formula
| Two component (varnish) | Diluent |
| (A component)) |
| HE6673 | 80 | XYL | 40 |
| EFKA3600 | 0.2 | TOL | 5 |
| BYK-306 | 0.3 | BAC | 25 |
| EFKA2018 | 0.1 | CAC | 15 |
| PMA | 8.0 | PMA | 15 |
| 10%sn | 0.4 | | |
| BAC/XYL | 11.0 | | |
| (B component) Bayer N3390 | | | |
A component: B component: diluent=100: 22: 80~100
6. Process conditions
▲ Baking condition: (1) 65℃ x 60min, place 24hours for test
(2) Air drying
▲ Substrate: Sand plate tin
7. Test technical index
| Test Item | Test Method | Reference Standard | Test Standard | Test Result
(reference value) |
| Surface drying | Blow cotton ball method | ------ | Not stick cotton ball | 32min(25um) |
| Hard drying | Finger pressing method | ------ | No finger print | 24h(25um) |
| 8h hardness | Pencil scratch | GB/T6739-96 | ----- | <HB |
| 24h hardness | Pencil scratch | GB/T6739-96 | ----- | HB |
| Gloss | 60 degree | GB/T9754-88 | ≥90 | 112 |
| Hardness | Pencil scratch | GB/T6739-96 | ≥2H | 2H |
| Impact | Impact method | GB/T1732-93 | ≥30kg.cm | 50cm(25μm) |
| Flexibility | Bending method | GB/T1731-93 | ≤2mm | 1mm |
| Adhesion | The case method | GB/T9286-98 | 100% | 100% |
| Fullness | Visual method | ----- | Excellent fullness, good brightness | Excellent |
| Levelling property | Visual method | ----- | Flat and smooth, no shrinkage cavity | Qualified |
| Ageing resistance | QUV machine | ----- | 800h no color change, no
falling off, gloss loss rate≤1% | Qualified |
| Acid resistance | Soak method | GB/T9274-88 | 10%H2SO472h no bubbling, no falling off, no color change | Qualified |
Alkaline resistance
|
Soak method
|
GB/T9274-88
|
5%NaOH48h no bubbling, no falling off, no color change
|
Qualified
|
8. Safe storage and shelf life
1. Stored in cool and ventilation place, keep far away from heat
and fire resources, keep the container closed.
2. From production date, shelf life is 12months.
9. Packing specifications
200kg/pail (new metal pail)
10. Safety
This product contains solvent, must do safeguard procedure, handle
carefully, avoid contact with the skins and eyes, for other
details, please refer to MSDS of this product.