Home > Water Based Acrylic Resin >

Film-forming Styrene-acrylic Copolymer Emulsion with Solid Content 45±1% and Viscosity 800-1500 mPa.s for Kraft Paper Waterborne Overcoat Varnishes

Product Categories

Water Based Acrylic Resin [196]
Solid Acrylic Resin [107]
Water Based Polyester Resin [18]
Polyethylene Wax Emulsion [100]
Water Based Alkyd Resin [31]
Solvent Based Acrylic Resin [54]
Water Based Epoxy Resin [55]
Mirror Effect Ink [46]
Epoxy Curing Agent [10]
Water Based Hydroxyl Acrylic Resin [46]
Water Based Peelable Resin [46]
High Hardness Floor Coatings [17]
Resins For Wood Coatings [27]
Water Based Industrial Coating Resins [28]

Xiamen WangQin Chemical Technology Co., Ltd.

Trust Seal

Verified Supplier

Credit Check

Supplier Assessment

Contact Now

Buy cheap Film-forming Styrene-acrylic Copolymer Emulsion with Solid Content 45±1% and Viscosity 800-1500 mPa.s for Kraft Paper Waterborne Overcoat Varnishes from wholesalers

Film-forming Styrene-acrylic Copolymer Emulsion with Solid Content 45±1% and Viscosity 800-1500 mPa.s for Kraft Paper Waterborne Overcoat Varnishes

Ask Lasest Price
Brand Name :	WeiLi Resin®
Model Number :	WQ-224
Certification :	ISO9001
Price :	Negotiable
Payment Terms :	L/C,T/T
Supply Ability :	500t/month
Delivery Time :	14work days

Add to Cart

Product Details
Company Profile

Film-forming Styrene-acrylic Copolymer Emulsion with Solid Content 45±1% and Viscosity 800-1500 mPa.s for Kraft Paper Waterborne Overcoat Varnishes

Introduction

WQ-224 is a styrene-acrylic copolymer emulsion capable of self-crosslinking at ambient temperature, specifically engineered for use in water-based topcoat varnishes and printing inks. It exhibits excellent compatibility with commonly available acrylic polymers. Furthermore, this product demonstrates effective pigment wetting in flexographic and gravure ink applications.

Physical Property:

Appearance	Translucent milky emulsion
Solid content (%)	45±1
Viscosity (mPa.s)	800-1500
Acid value	50
pH value	8.0-9.0
Density(g/l)	1.02-1.05
Particle size(μm)	0.10-0.20
MFFT (℃)	<0
Tg(℃)	-25

Performance:

◆ Minimal odor, low VOC emissions, and effective anti-adhesion characteristics
◆ Economical self-crosslinking film-forming emulsion with high cost efficiency
◆ Outstanding wear resistance and strong substrate adhesion
◆ Superior resistance to water and oils
◆ Exceptional color development and vibrancy

Application

◆ High-adhesive ink and varnish

◆ Plastic film ink and Varnish

◆ Water based UV primer

◆ Highly definition ink

Special Tips

The information herein is based on our current knowledge and experience.Technical recommendations are offered in good faith but are not guaranteed to be suitable for all applications.All data and suggestions should be considered as guidelines for evaluation and are not product specifications.

Product Tags:

Film-forming Styrene-acrylic Copolymer Emulsion with Solid Content 45±1% and Viscosity 800-1500 mPa.s for Kraft Paper Waterborne Overcoat Varnishes

Inquiry Cart 0

Send your message to this supplier


*From:	Your email address is incorrect!
*To:	Xiamen WangQin Chemical Technology Co., Ltd.
*Subject:	Subject is empty!
*Message:	For the best results, we recommend including the following details: -Self introduction -Required specifications -Inquire about price/MOQ Characters Remaining: (0/3000) Please enter 20 to 3000 characters to contact this supplier!

Explore more Water Based Acrylic Resin products from this supplier

Find Similar Products By Category:

Chemicals

Hot Searches:

Xiamen WangQin Chemical Technology Co., Ltd.

Film-forming Styrene-acrylic Copolymer Emulsion with Solid Content 45±1% and Viscosity 800-1500 mPa.s for Kraft Paper Waterborne Overcoat Varnishes

Film-forming Styrene-acrylic Copolymer Emulsion with Solid Content 45±1% and Viscosity 800-1500 mPa.s for Kraft Paper Waterborne Overcoat Varnishes

Film-forming Styrene-acrylic Copolymer Emulsion with Solid Content 45±1% and Viscosity 800-1500 mPa.s for Kraft Paper Waterborne Overcoat Varnishes

styrene-acrylic copolymer emulsion for kraft paper

waterborne overcoat varnishes acrylic resin

printing inks with pigment wetting

Film-forming Styrene-acrylic Copolymer Emulsion with Solid Content 45±1% and Viscosity 800-1500 mPa.s for Kraft Paper Waterborne Overcoat Varnishes