Non-film Forming Hard Styrene Acrylic Copolymer Emulsion with Solid Content 45±1% and Viscosity 400-900 cps for Water Based Flexo and Gravure Printing

Product Categories

Water Based Acrylic Resin [196]
Solid Acrylic Resin [107]
Water Based Polyester Resin [18]
Polyethylene Wax Emulsion [100]
Water Based Alkyd Resin [31]
Solvent Based Acrylic Resin [54]
Water Based Epoxy Resin [55]
Mirror Effect Ink [46]
Epoxy Curing Agent [10]
Water Based Hydroxyl Acrylic Resin [46]
Water Based Peelable Resin [46]
High Hardness Floor Coatings [17]
Resins For Wood Coatings [27]
Water Based Industrial Coating Resins [28]

Xiamen WangQin Chemical Technology Co., Ltd.

Trust Seal

Verified Supplier

Credit Check

Supplier Assessment

Contact Now

Buy cheap Non-film Forming Hard Styrene Acrylic Copolymer Emulsion with Solid Content 45±1% and Viscosity 400-900 cps for Water Based Flexo and Gravure Printing from wholesalers

Non-film Forming Hard Styrene Acrylic Copolymer Emulsion with Solid Content 45±1% and Viscosity 400-900 cps for Water Based Flexo and Gravure Printing

Ask Lasest Price
Brand Name :	WeiLi Resin®
Model Number :	WQ-2011L
Certification :	ISO9001
Price :	Negotiable
Payment Terms :	L/C,T/T
Supply Ability :	500t/month
Delivery Time :	14work days

Add to Cart

Product Details
Company Profile

Non-film Forming Hard Styrene Acrylic Copolymer Emulsion with Solid Content 45±1% and Viscosity 400-900 cps for Water Based Flexo and Gravure Printing

Introduction

WQ-2011L is a hard, non-film-forming styrene-acrylic copolymer emulsion, engineered specifically for formulating high-performance water-based overprint varnishes (WBOV) and printing inks. Varnishes based on WQ-2011L exhibit rapid curing, a superior glossy finish, outstanding water resistance, and exceptional block resistance. Furthermore, it delivers excellent pigment wetting and dispersion characteristics for water-based flexographic and gravure ink applications.

Physical Property

Appearance	Translucent milky emulsion
Solid content (%)	45±1
Viscosity at 25℃,cps(Brookfield, LVT No.4,60 RPM )	400-900
Acid value	51
pH value	8.0-9.0
Density(g/l)	1.02-1.05
Particle size(μm)	0.20-0.30
MFFT (℃)	>90
Tg(℃)	+98

Performance

◆Features rapid curing,

◆high-gloss finish,

◆exceptional clarity,

◆superior abrasion resistance,

◆excellent anti-blocking properties

Application

◆ Water based overprint varnishes

◆ Water based flexo and gravure printing inks

Special Tips

This information is prepared according to our existing knowledge and experience. While the technical

recommendations are provided in good faith, they may not suit every sample or formulation.

All data is intended as a guideline only.

Product Tags:

Non-film Forming Hard Styrene Acrylic Copolymer Emulsion with Solid Content 45±1% and Viscosity 400-900 cps for Water Based Flexo and Gravure Printing

Inquiry Cart 0

Send your message to this supplier


*From:	Your email address is incorrect!
*To:	Xiamen WangQin Chemical Technology Co., Ltd.
*Subject:	Subject is empty!
*Message:	For the best results, we recommend including the following details: -Self introduction -Required specifications -Inquire about price/MOQ Characters Remaining: (0/3000) Please enter 20 to 3000 characters to contact this supplier!

Explore more Water Based Acrylic Resin products from this supplier

Find Similar Products By Category:

Chemicals

Hot Searches:

Xiamen WangQin Chemical Technology Co., Ltd.

Non-film Forming Hard Styrene Acrylic Copolymer Emulsion with Solid Content 45±1% and Viscosity 400-900 cps for Water Based Flexo and Gravure Printing

Non-film Forming Hard Styrene Acrylic Copolymer Emulsion with Solid Content 45±1% and Viscosity 400-900 cps for Water Based Flexo and Gravure Printing

Non-film Forming Hard Styrene Acrylic Copolymer Emulsion with Solid Content 45±1% and Viscosity 400-900 cps for Water Based Flexo and Gravure Printing

water based acrylic resin emulsion

non-film forming styrene acrylic copolymer

flexo gravure printing ink resin

Non-film Forming Hard Styrene Acrylic Copolymer Emulsion with Solid Content 45±1% and Viscosity 400-900 cps for Water Based Flexo and Gravure Printing